Fracture, Fatigue, and Structural Integrity of Metallic Materials and Components Undergoing Random or Variable Amplitude Loadings

• Outros Autores: Benasciutti, Denis (Editor), Whittaker, Mark (Editor), Dirlik, Turan (Editor)
• Formato: Recurso Electrónico Capítulo de Livro
• Idioma: inglês
• Publicado em: Basel MDPI - Multidisciplinary Digital Publishing Institute 2022
• Assuntos: Technology: general issues; History of engineering & technology; small cracks; helicopter flight load spectra; FALSTAFF flight load spectra; fatigue crack growth; surface topography; optical profilometry; height digital image correlation; discontinuous displacements; triaxial displacements; fracture analysis; welded joint; repair welding thermal shock; XFEM; welding linear energy; high-temperature fatigue; nickel-based superalloy; investment casting; metallography; turbine blade; fatigue; testing systems; random loadings; servo-hydraulic; shaker table; crack growth; metallic materials; plasticity; crack closure; spectrum loading; random loading; fatigue damage; power spectral density (PSD); spectral methods; lattice structures; structural dynamic response; vibration fatigue testing; fatigue life prediction; analytical framework; fatigue crack; residual strength; retardation effect; nonstationary random loadings; run test; short-time Fourier transform; n/a
• Acesso em linha: DOAB: download the publication; DOAB: description of the publication

Most metallic components and structures are subjected, in service, to random or variable amplitude loadings. There are many examples: vehicles subjected to loadings and vibrations caused by road irregularity and engine, structures exposed to wind, off-shore platforms undergoing wave-loadings, and so...