Surface microhardness of different thicknesses of a premixed bioceramic material with or without the application of a moist cotton pellet

• Main Authors: Noushin Shokouhinejad (Author), Hassan Razmi (Author), Mehrfam Khoshkhounejad (Author), Arezoo Javani (Author), Maryam Raoof (Author)
• Format: Book
• Published: Wolters Kluwer Medknow Publications, 2016-01-01T00:00:00Z.
• Subjects: article
• Online Access: Connect to this object online.

Summary

Background: This study was conducted to assess the effect of thickness and hydration condition on the surface microhardness of Endosequence Root Repair Material putty (ERRM; Brasseler USA, Savannah, GA), a premixed bioceramic material. Materials and Methods: Polymethyl methacrylate cylindrical molds with an internal diameter of 4 mm and three heights of 2, 4, and 6 mm were fabricated. In Group 1 (dry condition), the molds with heights of 2, 4, and 6 mm (10 molds of each) were filled with ERRM. In Groups 2 and 3 (wet condition), a distilled water- or phosphate-buffered saline (PBS)-moistened cotton pellet was placed directly on the upper surface of ERRM, respectively. The lower surface of ERRM was in contact with floral foams soaked with human blood. After 4 days, Vickers microhardness of the upper surface of ERRM was tested. The data were analyzed using two-way analysis of variance. Significance level was set at P < 0.05. Results: No significant difference was found between the microhardness of three thicknesses of ERRM (2, 4, and 6 mm) with or without placing a distilled water- or PBS-moistened cotton pellet over the material (P > 0.05). Conclusion: Based on the results of this study, it could be concluded that placing a moistened cotton pellet on ERRM putty up to 6 mm thick might be unnecessary to improve its surface microhardness and hydration characteristics.

Item Description

1735-3327
2008-0255
10.4103/1735-3327.174715