nfluence of phosphate buffered saline on the bond strength of endodontic cement to dentin

• 主要な著者: Bruna Casagrande Cechella (著者), Josiane de Almeida (著者), Mara Cristina Santos Felippe (著者), Cleonice da Silveira Teixeira (著者), Eduardo Antunes Bortoluzzi (著者), Wilson Tadeu Felippe (著者)
• フォーマット: 図書
• 出版事項: Universidade Estadual de Campinas, 2015-07-01T00:00:00Z.
• 主題: article
• オンライン･アクセス: Connect to this object online.

要約

Aim: To analyze the influence of exposure and time of exposure to phosphate buffered saline (PBS) on the push-out bond strength (BS) of Biodentine to dentine. Methods: Eighty 2-mm-thick dentin discs were obtained from transversal sections of human teeth roots. The space of the canal was enlarged using #2-#5 Gates-Glidden burs to obtain 1.3-mm-diameter standardized cavities. The discs were immersed in 17% EDTA followed by 1% NaOCl and dried. The spaces of the canals were filled with Biodentine and the samples were divided into 2 groups (n=40) according to the storage: G1: exposure to moistened cotton pellet; G2: exposure to PBS. After 30 min, 1, 3 and 28 days, 10 samples of each group were subjected to the push-out test. Data were analyzed using ANOVA and Tukey test (p < 0.05). Results: The specimens exposed to PBS had lower BS (p < 0.05), except for the 1-day period (p = 0.6017). In specimens of Group 1 the BS increased up to 3 days (p < 0.05). In specimens in Group 2, the BS increased from 30 min to 1 day (p < 0.0001) and remained stable up to 3 days (p = 0.9876). At 28 days, a significant decrease was observed in the BS values of both groups (p < 0.05). Conclusions: The exposure of Biodentine to PBS led to lower BS values. In general, the BS increased gradually up to 3 days and reduced at 28 days.

記述事項

10.20396/bjos.v14i2.8640826
1677-3225