Evaluation of microleakage for three types of light cure orthodontic band cement

• Main Author: Lara Riyadh Al-Banaa (Author)
• Format: Book
• Published: Elsevier, 2022-05-01T00:00:00Z.
• Subjects: article
• Online Access: Connect to this object online.

Summary

Objective: The aim of this study was to compare the microleakage of three types of light cure orthodontic band cement (Resilience, Band-it and Transbond Plus) and to compare low and high curing light intensities at the enamel-cement and band-cement interfaces in the gingival and occlusal margins. Materials and methods: Sixty extracted human premolars were divided into six groups (n = 10 specimens) according to the type of cement used and intensity of light cure. Microetched bands of upper premolars cemented to the teeth by Transbond Plus (3 M Unitek), Resilience (Orthotechnology) and Band-it (db Orthodontics). Three groups were cured by a standard mode light cure (over 900 mw/cm2) for 20 s, and the other three groups were cured with an extra mode light cure (over 2700 mw/cm2) for 6 s. The teeth were sealed by nail varnish and immersed for 24 h in 0.5% basic fuchsin solution. After that, the teeth were sectioned in the buccoligual direction, observed under a stereomicroscope, and then recorded for microleakage at the enamel-cement and band-cement interfaces in the gingival and occlusal margins. The statistical analysis was performed using Kruskal-Wallis and Mann-Whitney U tests, and the level of significance was set at P < 0.05. Result: The microleakage scores showed no significant differences at the enamel-cement and band-cement interfaces among the three types of orthodontic band cement subjected to low- and high-intensity curing light. Conclusions: The type of cement and intensity of light cure did not affect the amount of microleakage at either interface.

Item Description

2212-4268
10.1016/j.jobcr.2022.04.004