The Effect of Sodium Hypochlorite on Shear Bond between Composite and Porcelain Specimens
Aim of Study: This in vitro study was conducted to evaluate the shear bond strength of intra oral por-celain repair system using 10% sodium hypochlorite and different acid etch. Materials and methods: Forty specimens were prepared in form of metal disks (8mm in diameter, 15mm height) and porcelain w...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Book |
| Published: |
University of Mosul, College of Dentistry,
2012-08-01T00:00:00Z.
|
| Subjects: | |
| Online Access: | Connect to this object online. |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Aim of Study: This in vitro study was conducted to evaluate the shear bond strength of intra oral por-celain repair system using 10% sodium hypochlorite and different acid etch. Materials and methods: Forty specimens were prepared in form of metal disks (8mm in diameter, 15mm height) and porcelain was applied according to the manufacturer instructions.The specimens randomly divided into 4 equal groups. In Group I ,II the samples were treated with 9% hydrofluoric acid for one minute. While groups III, IV were treated with 37% phosphoric acid for one minute, after washing the specimens with water and dryness, groups II, III the surfaces treated with 10%sodium hypochlorite for one minute while group I and IV leaved untreated. After that, the surfaces of all samples were washed and dried and silane coupling agent (MonoBond-S Vivadent, Liechtenstein) was applied according to the manu-facturer instructions, then bonding agent (Excite) (Vivadent, Liechtenstein) and composite (tetric N-ceram) (Vivadent, Liechtenstein) were applied according to the manufacturer instructions. All the sam-ples were stored in normal physiological saline for 7 days. Then the samples were thermocycled ma-nually between two water baths After that Shear bond strength was tested using universal testing ma-chine. Results: using ANOVA and Duncan's multiple range tests. The result showed that there was highly significant difference between groups treated with 10%sodium hypochlorite with untreated one. There was significant difference between samples acid etched using hydrofluoric acid with those etched with phosphoric acid. Conclusions: Sodium hypochlorite and hydrofluoric acid significantly increase the shear bond strength between composite resin and porcelain fused to metal specimens |
|---|---|
| Item Description: | 10.33899/rden.2012.65069 1812-1217 1998-0345 |