Comparative analysis of endocrown fracture resistance and marginal adaptation: CAD/CAM technology using lithium disilicate vs. zirconia-reinforced lithium silicate ceramics
Aims: The present study aimed to compare the fracture resistance and marginal adaptation of endocrowns fabricated using lithium disilicate (LDS) and zirconia-reinforced lithium silicate 9ZLS) ceramics by the computer-aided design and computer-aided manufacturing (CAD/CAM) technology. Materials and M...
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Book |
| Published: |
Elsevier,
2024-02-01T00:00:00Z.
|
| Subjects: | |
| Online Access: | Connect to this object online. |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Aims: The present study aimed to compare the fracture resistance and marginal adaptation of endocrowns fabricated using lithium disilicate (LDS) and zirconia-reinforced lithium silicate 9ZLS) ceramics by the computer-aided design and computer-aided manufacturing (CAD/CAM) technology. Materials and Methods: In this in vitro experimental study, 24 extracted mandibular first molars received standard endocrown preparation and were randomly assigned to two groups (n = 12) for the fabrication of endocrowns with ZLS (Suprinity) and LDS (IPS e.max CAD) ceramics. After scanning the teeth with a CAD scanner, endocrowns were designed by inLab Software version 15 (inLab SW 15) and prepared by an imes-icore 350i milling machine. The vertical marginal gap of endocrowns was measured under a stereomicroscope at three steps before and after cementation and after thermomechanical cycles. The fracture resistance of specimens was then measured by load application at a 45° angle. Mode of failure was also determined as reparable or irreparable. Data were analyzed using Pearson's correlation test and t-test. Results: The mean fracture resistance of ZLS endocrowns was significantly higher than that of LDS endocrowns (P = 0.000). The reparability of ZLS endocrowns was zero, while that of LDS endocrowns was 83.33 %. The vertical marginal gap was significantly smaller in ZLS than in LDS endocrowns at all three time points (P < 0.05). Also, the marginal gap increased by cementation and thermomechanical cycles in both groups. Conclusion: ZLS and LDS endocrowns both showed acceptable vertical marginal adaptation. ZLS had superior marginal adaptation and higher fracture resistance. |
|---|---|
| Item Description: | 1013-9052 10.1016/j.sdentj.2023.11.020 |