MDP-salts as an adhesion promoter with MDP-primers and self-adhesive resin cement for zirconia cementation
Abstract Purpose To evaluate the effect of zirconia priming with MDP-Salt before MDP containing primers and self-adhesive cement on the shear bond strength. Materials and methods Fully sintered high translucent zirconia specimens (n = 120) were assigned into 2 groups (n = 60 each): Control (No Pretr...
Saved in:
| Main Authors: | , , , , , , |
|---|---|
| Format: | Book |
| Published: |
BMC,
2023-11-01T00:00:00Z.
|
| Subjects: | |
| Online Access: | Connect to this object online. |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Abstract Purpose To evaluate the effect of zirconia priming with MDP-Salt before MDP containing primers and self-adhesive cement on the shear bond strength. Materials and methods Fully sintered high translucent zirconia specimens (n = 120) were assigned into 2 groups (n = 60 each): Control (No Pretreatment) and Methacryloyloxydecyl dihydrogen phosphate salt (MDP-Salt) pretreated. Each group was divided into 3 subgroups (n = 20) according to cementation protocol: 1) MDP + Silane primer and conventional resin cement, 2) MDP+ Bisphenyl dimethacrylate (BPDM) primer and conventional resin cement, and 3) MDP containing self-adhesive resin cement. Shear bond strength (SBS) was measured after 10,000 thermocycling. Contact angle was measured for tested groups. Surface topography was assessed using a 3D confocal laser scanning microscope (CLSM). Weibull analysis was performed for SBS and one-way ANOVA for contact angle and surface topography measurements (α = 0.05). Results The use of MDP-Salt significantly improved the SBS (p < .05) for all tested subgroups. Self-adhesive cement showed an insignificant difference with MDP + Silane group for both groups (p > .05). MDP + BPDM showed a significantly lower characteristic strength compared to self-adhesive resin cement when both were pretreated with MDP-Salt. No difference between all tested groups in the surface topographic measurements while MDP-Salt showed the highest contact angle. Conclusion MDP-Salt pretreatment can improve bonding performance between zirconia and MDP containing products. |
|---|---|
| Item Description: | 10.1186/s12903-023-03663-y 1472-6831 |