Enhanced levitation force of partial melted (Y,Er)Ba2Cu3O7-8 superconductors with formation of minor 211 phase / Ahmad Kamal Yahya, Suzi Ahmad and Imad Hamadneh
Y0.5 Er 0.5 Ba2 Cu307-8 superconductors with Er2 O3 addition were prepared by partial melting and the effects of excess Er2 03 addition on the magnetic levitation force (MLF) of the partial-melted samples have been investigated. A non-linear relationship was observed between the MLF measured at 77 K...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Book |
| Published: |
Faculty of Applied Sciences,
2005.
|
| Subjects: | |
| Online Access: | Link Metadata |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Y0.5 Er 0.5 Ba2 Cu307-8 superconductors with Er2 O3 addition were prepared by partial melting and the effects of excess Er2 03 addition on the magnetic levitation force (MLF) of the partial-melted samples have been investigated. A non-linear relationship was observed between the MLF measured at 77 K and the amount of Er2 O3. It was found that the optimum amount of excess Er2 O3 for enhanced MLF is 10 wt.%. X-ray powder diffraction analysis showed formation of major 123 phase with minor 211 non-superconducting phase for all samples. The results were discussed in detail and the presence of 211 impurities is suggested to act as pinning centers in the 123 samples. |
|---|---|
| Item Description: | https://ir.uitm.edu.my/id/eprint/11790/1/AJ_AHMAD%20KAMAL%20YAHYA%20SL%2005.pdf |