Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor
Fabrication of the Bi-based tapes started with the preparation of its precursor powder with composition of Bi1.8 Pb 0.4 Sr2 Ca2.2 Cu3 O10+y. The post-annealed powder with a majority of 2212 phase was then ground before it was packed into a silver tube. Then the composite was sway-rolled and drawn in...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Book |
| Published: |
Faculty of Applied Sciences,
2005.
|
| Subjects: | |
| Online Access: | Link Metadata |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
MARC
| LEADER | 00000 am a22000003u 4500 | ||
|---|---|---|---|
| 001 | repouitm_11791 | ||
| 042 | |a dc | ||
| 100 | 1 | 0 | |a Lau, K.T. |e author |
| 700 | 1 | 0 | |a R-, Abd Shukor |e author |
| 245 | 0 | 0 | |a Bi-based mono-core superconductor tapes : fabrication process and the effect of the thermomechanical treatment on the transport properties / K.T. Lau and R-Abd Shukor |
| 260 | |b Faculty of Applied Sciences, |c 2005. | ||
| 500 | |a https://ir.uitm.edu.my/id/eprint/11791/1/AJ_K.T.%20LAU%20SL%2005.pdf | ||
| 520 | |a Fabrication of the Bi-based tapes started with the preparation of its precursor powder with composition of Bi1.8 Pb 0.4 Sr2 Ca2.2 Cu3 O10+y. The post-annealed powder with a majority of 2212 phase was then ground before it was packed into a silver tube. Then the composite was sway-rolled and drawn into wire with diameter of 1.08 mm. To make it into tape form, the wire was cut into shorter length before went through rolling process using a roller machine. The tapes were divided into sample groups and underwent different thermo-mechanical treatments. All the final processed Bi-based tapes had mixed superconductor phases of 2223 and 2212. Most part of HTSC grains in the tapes melted during the sintering. Transport voltage-current characteristics of the tapes was found to obey the power law relationship. The thermo-mechanical treatment was found necessary to improve the structural quality of the tapes. | ||
| 546 | |a en | ||
| 690 | |a Electricity and magnetism | ||
| 655 | 7 | |a Article |2 local | |
| 655 | 7 | |a PeerReviewed |2 local | |
| 787 | 0 | |n https://ir.uitm.edu.my/id/eprint/11791/ | |
| 856 | 4 | 1 | |u https://ir.uitm.edu.my/id/eprint/11791/ |z Link Metadata |