Low energy impact on the short kenaf fibre reinforced epoxy composites: effect to the residual strength and modulus / Syarifah Yunus ... [et al.]
In this investigation, the effect of low energy impact to the residual strength and modulus of short kenaf fibre reinforced epoxy composites were investigated. The composites were made from hand lay-out technique and subjected to low impact energy at the 20%, 25% and 30% of impact failure values. Th...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Book |
| Published: |
Faculty of Mechanical Engineering Universiti Teknologi MARA (UiTM),
2015.
|
| Subjects: | |
| Online Access: | Link Metadata |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
MARC
| LEADER | 00000 am a22000003u 4500 | ||
|---|---|---|---|
| 001 | repouitm_16148 | ||
| 042 | |a dc | ||
| 100 | 1 | 0 | |a Yunus, Syarifah |e author |
| 700 | 1 | 0 | |a Abdullah, Abdul Hakim |e author |
| 700 | 1 | 0 | |a Abdul Halim, Nurul Hayati |e author |
| 700 | 1 | 0 | |a Salleh, Zuraidah |e author |
| 700 | 1 | 0 | |a Md. Taib, Yakub |e author |
| 245 | 0 | 0 | |a Low energy impact on the short kenaf fibre reinforced epoxy composites: effect to the residual strength and modulus / Syarifah Yunus ... [et al.] |
| 260 | |b Faculty of Mechanical Engineering Universiti Teknologi MARA (UiTM), |c 2015. | ||
| 500 | |a https://ir.uitm.edu.my/id/eprint/16148/1/AJ_SYARIFAH%20YUNUS%20JME%2015.pdf | ||
| 520 | |a In this investigation, the effect of low energy impact to the residual strength and modulus of short kenaf fibre reinforced epoxy composites were investigated. The composites were made from hand lay-out technique and subjected to low impact energy at the 20%, 25% and 30% of impact failure values. The load-time curve exhibited the damage states of unreinforced epoxy specimens and short kenaf fibre reinforced epoxy composites. The research found that the low energy impacts were affecting the residual strength and residual stiffness which indicated the short kenaf fibre reinforced epoxy composites were extremely sensitive to the impact loads. The damages were manifest by the visible observation of cracks on the specimens | ||
| 546 | |a en | ||
| 690 | |a Polymers. Polymeric composites | ||
| 655 | 7 | |a Article |2 local | |
| 655 | 7 | |a PeerReviewed |2 local | |
| 787 | 0 | |n https://ir.uitm.edu.my/id/eprint/16148/ | |
| 787 | 0 | |n https://jmeche.uitm.edu.my/ | |
| 856 | 4 | 1 | |u https://ir.uitm.edu.my/id/eprint/16148/ |z Link Metadata |