The ion transport study in corn starch-NaHSO₃ based polymer electrolytes / Fatin Farhana Awang ... [et al.]
In this work, different amounts of sodium bisulfite, NaHSO3 (5wt.% to 40wt.%), were dissolved in a corn starch polymer host to synthesize solid polymer electrolyte (SPE) using a solution casting technique. Then, the films prepared were characterized using non-destructive electrical impedance spectro...
Сохранить в:
| Главные авторы: | , , , |
|---|---|
| Формат: | |
| Опубликовано: |
Universiti Teknologi MARA,
2021-08.
|
| Предметы: | |
| Online-ссылка: | Link Metadata |
| Метки: |
Добавить метку
Нет меток, Требуется 1-ая метка записи!
|
| Итог: | In this work, different amounts of sodium bisulfite, NaHSO3 (5wt.% to 40wt.%), were dissolved in a corn starch polymer host to synthesize solid polymer electrolyte (SPE) using a solution casting technique. Then, the films prepared were characterized using non-destructive electrical impedance spectroscopy to determine SPE films' conductivity and electrical transport properties. The highest conductivity of the sample at ambient temperature was recorded at 15wt. % of NaHSO3 with a value of 2.22 × 10-4 Scm-1. Moreover, the ion transport parameters at room temperature are found to be 2.41 × 10-7 cm2 s-1, 9.39 × 10-6 cm2 V-1s-1, 1.70 × 1019 cm-3 for D, µ and n, respectively. The conductivity of the samples was found dependent on diffusion coefficient, D and mobility, µ of ions. |
|---|---|
| Примечание: | https://ir.uitm.edu.my/id/eprint/51116/1/51116.pdf |