The properties of reconstituted panel manufactured from oil palm fronds / Chen Fung Woo and Suhaimi Muhammed
The reconstituted panels were manufactured from oil palm fronds for different board densities (560 kg/m3 to 800 kg/m3) and tested for various properties such as modulus of rupture (MOR), modulus of elasticity (MOE) and thickness swelling. The modulus of rupture (MOR) of the board at 10% resin level...
Saved in:
Main Authors: | , |
---|---|
Format: | Book |
Published: |
Universiti Teknologi MARA Cawangan Pahang,
2000.
|
Subjects: | |
Online Access: | Link Metadata |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
MARC
LEADER | 00000 am a22000003u 4500 | ||
---|---|---|---|
001 | repouitm_62097 | ||
042 | |a dc | ||
100 | 1 | 0 | |a Chen, Fung Woo |e author |
700 | 1 | 0 | |a Muhammed, Suhaimi |e author |
245 | 0 | 0 | |a The properties of reconstituted panel manufactured from oil palm fronds / Chen Fung Woo and Suhaimi Muhammed |
260 | |b Universiti Teknologi MARA Cawangan Pahang, |c 2000. | ||
500 | |a https://ir.uitm.edu.my/id/eprint/62097/1/62097.PDF | ||
520 | |a The reconstituted panels were manufactured from oil palm fronds for different board densities (560 kg/m3 to 800 kg/m3) and tested for various properties such as modulus of rupture (MOR), modulus of elasticity (MOE) and thickness swelling. The modulus of rupture (MOR) of the board at 10% resin level was 27.3 MPa, 26.6 MPa, 47.5 MPa and 96.0 MPa at densities 560 kg/m3, 640 kg/m3 ,720 kg/m3 and 800 kg/m3 respectively. This is equivalent to 30% to 90% of the average equivalent solid wood. The boards retained 30% to 60% of their strength and 70% to 90% of their stiffness after soaking in water. Thickness swelling decreased from 51% to 23%, and water absorption decreased from 152% to 59% when board density increased from 560 kg/m3 to 800 kg/m3. | ||
546 | |a en | ||
690 | |a Palm oil | ||
690 | |a Wood products. Furniture | ||
690 | |a Engineered wood. Fiberboard, particle board, etc. | ||
655 | 7 | |a Article |2 local | |
655 | 7 | |a PeerReviewed |2 local | |
787 | 0 | |n https://ir.uitm.edu.my/id/eprint/62097/ | |
856 | 4 | 1 | |u https://ir.uitm.edu.my/id/eprint/62097/ |z Link Metadata |