Influence of hydrochloric acid against food-grade steel SUS304 and its corrosion impact / Nur Dhiya Syariah Mazelam ... [et al.]
This study aims to investigate the progress of corrosion rate on stainless steel (SUS304) in hydrochloric acid (HCl) as exposed for 8 days. The HCl as a corrosive medium was used at pH 2 and pH 5. The evaluation of corrosion rate was done through weight loss measurement. Morphology and structure of...
Saved in:
Main Authors: | , , , , , |
---|---|
Format: | Book |
Published: |
UiTM Cawangan Negeri Sembilan,
2022.
|
Subjects: | |
Online Access: | Link Metadata |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
MARC
LEADER | 00000 am a22000003u 4500 | ||
---|---|---|---|
001 | repouitm_70069 | ||
042 | |a dc | ||
100 | 1 | 0 | |a Mazelam, Nur Dhiya Syariah |e author |
700 | 1 | 0 | |a Yahya, Solhan |e author |
700 | 1 | 0 | |a Ab. Ghani, Zaidi |e author |
700 | 1 | 0 | |a Ahmad, Zuliahani |e author |
700 | 1 | 0 | |a Samsudin, Dalina |e author |
700 | 1 | 0 | |a Muhd Zailani, Nabilah Akemal |e author |
245 | 0 | 0 | |a Influence of hydrochloric acid against food-grade steel SUS304 and its corrosion impact / Nur Dhiya Syariah Mazelam ... [et al.] |
260 | |b UiTM Cawangan Negeri Sembilan, |c 2022. | ||
500 | |a https://ir.uitm.edu.my/id/eprint/70069/1/70069.pdf | ||
520 | |a This study aims to investigate the progress of corrosion rate on stainless steel (SUS304) in hydrochloric acid (HCl) as exposed for 8 days. The HCl as a corrosive medium was used at pH 2 and pH 5. The evaluation of corrosion rate was done through weight loss measurement. Morphology and structure of metal specimens were characterized by optical microscope before and after immersion test. The results showed that the corrosion rates were increased significantly within 4 days of immersion. The corrosion rate in pH 2 reveals the highest values at 0.020 mm/y. While in pH 5, the rate of corrosion exhibits moderate value ranging from 0.006-0.011 mm/y. The corrosion behavior of the stainless steel coupon was influenced by the duration of exposure in the HCl medium. The concentration of hydrogen cations and aggressiveness of chloride anion in the corrosive medium has been associated with corrosion. | ||
546 | |a en | ||
690 | |a Metals | ||
690 | |a Oxidation | ||
690 | |a Acids and bases | ||
655 | 7 | |a Article |2 local | |
655 | 7 | |a PeerReviewed |2 local | |
787 | 0 | |n https://ir.uitm.edu.my/id/eprint/70069/ | |
856 | 4 | 1 | |u https://ir.uitm.edu.my/id/eprint/70069/ |z Link Metadata |