Karakteristik Komposit Serat Enceng Gondok Dengan Fraksi Volume 15%, 20%, 25% Terhadap Uji Bending, Uji Tarik Dan Daya Serap Bunyi Untuk Dinding Peredam Suara

• Main Authors: Heri Setyawan, Riyan (Author), , Wijianto, ST., M.Eng.Sc (Author), , Ir. Pramuko IP, MT (Author)
• Format: Book
• Published: 2016.
• Subjects: Thesis; NonPeerReviewed
• Online Access: Connect to this object online
• Notes: https://eprints.ums.ac.id/45940/1/PUBLIKASI%20ILMIAH.pdf; https://eprints.ums.ac.id/45940/4/COVER%20DLL.pdf; https://eprints.ums.ac.id/45940/7/BAB%20I.pdf; https://eprints.ums.ac.id/45940/8/BAB%20II.pdf; https://eprints.ums.ac.id/45940/12/BAB%20III.pdf; https://eprints.ums.ac.id/45940/15/BAB%20IV.pdf; https://eprints.ums.ac.id/45940/16/BAB%20V.pdf; https://eprints.ums.ac.id/45940/17/DAFTAR%20PUSTAKA.pdf; https://eprints.ums.ac.id/45940/22/LAMPIRAN.pdf; https://eprints.ums.ac.id/45940/23/PERNYATAAN%20PUBLIKASI%20ILMIAH.pdf
• Keywords: TJ Mechanical engineering and machinery

Purpose of the research is to know tensile strength and bending strength of water hyacinth (eceng gondok) composite at variation of volume fraction of 15%, 20% and 25% with standards of ASTM D 3039 and ASTM D 799-99, andalso, capability of sound absorption with sponge layer and plywood layer and without those layers are also researched with ANSI S1.13-05 standards. Primary material of the research is water hyacinth fiber with polyester matrix of BQTN 157. Main variable of the research is volume fractions of 15%, 20% and 25% fibers with procedure of tensile test referring to ASTM D 3039, the bending test refers to ASTM D 799-9 and the test of sound absorption refers to ANSI S1.13-05. Results of the research indicated that the average highest tensile strength of was found at volume fraction of 25%, namely 131.76 MPa and the lowest one was found at volume fraction of 15%, namely 59.69 MPa and the average highest modulus of elasticity was found at volume fraction of 25%, namely 17989.61 MPa and the lowest one was found at volume fraction of 15%, namely 8149.27 MPA. The average highesttensile strength of 30.41 MPa was found at volume fraction of 25% and the lowest one of 12.43 MPa was found at volume fraction of 15% and the average highest modulus of elasticityof 1265.15 MPa was found at volume fraction of 25% and the lowest one of 996.82 was found at volume fraction of 15%. The highest sound absorption without plywood and plank layers was found at volume fraction of 25%, namely 1.34 dB and the lowest one was found at volume fraction of 15%, namely 0.21 dB. While, the highest value of sound absorption with the use of layers was found at volume fraction of 25%, namely 1.66 dB and the lowest one was found at volume fraction of 15%, namely 0.67 dB.