PEMBUATAN NANOFLUIDA Al2O3 DARI NANOPARTIKEL Al2O3 HASIL SINTESIS MENGGUNAKAN METODE SOL GEL DENGAN TEPUNG TAPIOKA SEBAGAI CAPPING AGENT UNTUK APLIKASI DI RADIATOR

• Main Author: Diki Yuliardi, - (Author)
• Format: Book
• Published: 2020-08-28.
• Subjects: Thesis; NonPeerReviewed
• Online Access: Link Metadata
• Notes: http://repository.upi.edu/53175/1/S_FIS_1403489_Title.pdf; http://repository.upi.edu/53175/2/S_FIS_1403489_Chapter1.pdf; http://repository.upi.edu/53175/3/S_FIS_1403489_Chapter2.pdf; http://repository.upi.edu/53175/4/S_FIS_1403489_Chapter3.pdf; http://repository.upi.edu/53175/5/S_FIS_1403489_Chapter4.pdf; http://repository.upi.edu/53175/6/S_FIS_1403489_Chapter5.pdf; http://repository.upi.edu/53175/7/S_FIS_1403489_Appendix.pdf
• Keywords: L Education (General); QC Physics

Pembuatan nanofluida air-Al2O3 dari nanopartikel Al2O3 hasil sintesis menggunakan metode sol gel dengan tepung tapioka sebagai capping agent untuk aplikasi di radiator telah dilakukan. Nanofluida air-Al2O3 disintesis menggunakan metode dua langkah (Two step method) dengan dua konsentrasi berbeda yaitu 0,1 %wt dan 0,2 %wt. Pengujian heat transfer pada penelitian ini menggunakan set alat radiator dengan menjaga tetap laju aliran fluida dan suhu inlet sebesar 3,3 LPM (liter/menit) dan 50oC. Serbuk nanopartikel Al2O3 dikarakterisasi menggunakan X-ray diffraction (XRD) dan Surface Area Meter. Hasil karakterisasi XRD menunjukkan nanopartikel Al2O3 yang telah disintesis merupakan alpha-Al2O3. Ukuran kristal dan ukuran partikel nanopartikel Al2O3 sebesar 36,25 nm dan 80,47 nm. Potensial zeta nanofluida air-Al2O3 yang dihasilkan sebesar -35,26 mV dan -37,83 mV untuk konsentrasi 0,1 %wt dan 0,2 %wt. Penambahan konsentrasi pada nanofluida meningkatkan heat transfer pada radiator. Convective Heat Transfer Coefficient dan Overall Heat Transfer Coefficient masing-masing meningkat sebesar 139,52% dan 168,31% dibandingkan air sebagai fluida dasar. Fabrication of water-Al2O3 nanofluids from Al2O3 nanoparticles synthesized using sol gel method with tapioca starch as capping agent for application in radiator were succesful. Water-Al2O3 nanofluids synthesized with two step method with two different concentration 0,1 %wt and 0,2 %wt. Heat transfer test in this study using radiator machine with constant fluids flow and inlet temperature with 3,3 LPM (liter/minute) and 50oC. The powder of Al2O3 nanoparticles were characterization with X-ray diffraction (XRD) and Surface Area Meter. The result of XRD analysis show Al2O3 nanoparticles was synthesized is alpha-Al2O3. Crystallize and particle size of Al2O3 nanoparticles was 36,25 nm and 80,47 nm. Zeta potential of water-Al2O3 nanofluids was -35,26 mV and -37,83 mV for Al2O3 concentrations of 0,1 %wt and 0,2 %wt. Addition of concentration of nanofluids increases heat transfer of radiator. Convective Heat Transfer Coefficient and Overall Heat Transfer Coefficient increases up to 139,52% and 168,31% compared with water as base fluids.