Investigation of Microstructural and Corrosion Properties of Steels and Light Alloys

• Eará dahkkit: Gennari, Claudio (Doaimmaheaddji), Pezzato, Luca (Doaimmaheaddji)
• Materiálatiipa: Elektrovnnalaš Girjji oassi
• Giella: eaŋgalasgiella
• Almmustuhtton: Basel MDPI - Multidisciplinary Digital Publishing Institute 2023
• Fáttát: Technology: general issues; History of engineering & technology; chloride concentration; crevice corrosion; relative humidity; stainless steel; stress corrosion cracking; high-silicon steel; austempering; retained austenite; corrosion resistance; ultra-low carbon bainite steel; niobium microalloying; mechanical property; corrosion behavior; API-X100 pipeline; bitumen; corrosion; inclusion; dust; Ni-based superalloys; micro laser powder bed fusion; heat treatment; mechanical properties; Galvalume; Plasma Electrolytic Oxidation; antifouling; anti-corrosion coatings; additive manufacturing (AM); titanium alloys; aluminum alloys; duplex stainless steels; defects; steel microstructure; post-fire properties; fracture surface; brittle cracking; impact test; shear fracture appearance; toughness; laser welding; aluminum alloy; zirconium; fusion zone; micro-galvanic; interdendritic segregation; passive film; n/a
• Liŋkkat: DOAB: download the publication; DOAB: description of the publication

According to the latest NACE estimation (2013), the global cost of corrosion is equivalent to approximately 3.4% of the global GDP (2.5 trillion US dollars), not considering environmental consequences or safety issues. A reduction between 15% and 35% could be realized if prevention techniques and pr...