A preliminary study on the properties oil palm board: Effect of resin content / Nurrohana Ahmad ... [et al.]
Three-layer oil palm boards were produced using urea formaldehyde resin. Face and back layer particles were sprayed with 10%, 12% and 14% resin while the core was maintained at 10% resin content. The oil palm board was hot-pressed at 165°C for 6 minutes at a pressure of 120 kgcm-2. With increasing r...
Zapisane w:
| Główni autorzy: | , , , , |
|---|---|
| Format: | Książka |
| Wydane: |
Universiti Teknologi MARA Cawangan Pahang,
2007-10.
|
| Hasła przedmiotowe: | |
| Dostęp online: | Link Metadata |
| Etykiety: |
Dodaj etykietę
Nie ma etykietki, Dołącz pierwszą etykiete!
|
| Streszczenie: | Three-layer oil palm boards were produced using urea formaldehyde resin. Face and back layer particles were sprayed with 10%, 12% and 14% resin while the core was maintained at 10% resin content. The oil palm board was hot-pressed at 165°C for 6 minutes at a pressure of 120 kgcm-2. With increasing resin content, all the mechanical and physical properties improved significantly. However, all board properties did not meet the minimum requirement of the BS 5669. |
|---|---|
| Deskrypcja: | https://ir.uitm.edu.my/id/eprint/36025/1/36025.PDF |