A preliminary study on the properties oil palm board: Effect of resin content / Nurrohana Ahmad ... [et al.]
Three-layer oil palm boards were produced using urea formaldehyde resin. Face and back layer particles were sprayed with 10%, 12% and 14% resin while the core was maintained at 10% resin content. The oil palm board was hot-pressed at 165°C for 6 minutes at a pressure of 120 kgcm-2. With increasing r...
Tallennettuna:
| Päätekijät: | , , , , |
|---|---|
| Aineistotyyppi: | Kirja |
| Julkaistu: |
Universiti Teknologi MARA Cawangan Pahang,
2007-10.
|
| Aiheet: | |
| Linkit: | Link Metadata |
| Tagit: |
Lisää tagi
Ei tageja, Lisää ensimmäinen tagi!
|
| Yhteenveto: | Three-layer oil palm boards were produced using urea formaldehyde resin. Face and back layer particles were sprayed with 10%, 12% and 14% resin while the core was maintained at 10% resin content. The oil palm board was hot-pressed at 165°C for 6 minutes at a pressure of 120 kgcm-2. With increasing resin content, all the mechanical and physical properties improved significantly. However, all board properties did not meet the minimum requirement of the BS 5669. |
|---|---|
| Huomautukset: | https://ir.uitm.edu.my/id/eprint/36025/1/36025.PDF |