The properties of reconstituted panel manufactured from oil palm fronds / Chen Fung Woo and Suhaimi Muhammed
The reconstituted panels were manufactured from oil palm fronds for different board densities (560 kg/m3 to 800 kg/m3) and tested for various properties such as modulus of rupture (MOR), modulus of elasticity (MOE) and thickness swelling. The modulus of rupture (MOR) of the board at 10% resin level...
Guardado en:
| Autores principales: | , |
|---|---|
| Formato: | Libro |
| Publicado: |
Universiti Teknologi MARA Cawangan Pahang,
2000.
|
| Materias: | |
| Acceso en línea: | Link Metadata |
| Etiquetas: |
Agregar Etiqueta
Sin Etiquetas, Sea el primero en etiquetar este registro!
|
| Sumario: | The reconstituted panels were manufactured from oil palm fronds for different board densities (560 kg/m3 to 800 kg/m3) and tested for various properties such as modulus of rupture (MOR), modulus of elasticity (MOE) and thickness swelling. The modulus of rupture (MOR) of the board at 10% resin level was 27.3 MPa, 26.6 MPa, 47.5 MPa and 96.0 MPa at densities 560 kg/m3, 640 kg/m3 ,720 kg/m3 and 800 kg/m3 respectively. This is equivalent to 30% to 90% of the average equivalent solid wood. The boards retained 30% to 60% of their strength and 70% to 90% of their stiffness after soaking in water. Thickness swelling decreased from 51% to 23%, and water absorption decreased from 152% to 59% when board density increased from 560 kg/m3 to 800 kg/m3. |
|---|---|
| Notas: | https://ir.uitm.edu.my/id/eprint/62097/1/62097.PDF |