Effects of waste paper sludge ash on compressive strength of concrete cubes / Marzuki A.Rahman ...[et al.]
Waste paper sludge incinerator ash (WPSIA) was investigated for its potential use as a replacement for cement in concrete. The physical and chemical properties of raw materials were determined. The water cement ratio was fixed at 0.55 while WPSIA was used at 5%, 10%, 15%, 20%, 25% and 30% replacemen...
Shranjeno v:
| Main Authors: | , , , , |
|---|---|
| Format: | Knjiga |
| Izdano: |
2006.
|
| Teme: | |
| Online dostop: | Link Metadata |
| Oznake: |
Označite
Brez oznak, prvi označite!
|
| Izvleček: | Waste paper sludge incinerator ash (WPSIA) was investigated for its potential use as a replacement for cement in concrete. The physical and chemical properties of raw materials were determined. The water cement ratio was fixed at 0.55 while WPSIA was used at 5%, 10%, 15%, 20%, 25% and 30% replacement by weight of cement. The grade design of proportions was 30 N/mm2. Slump and compressive strengths were performed on all specimens. Results indicate the WPSA caused a reduction in slump values when it was used as a cement replacement. The replacement of WPSIA up 30% exhibited, generally similar to control mix (0% WPSIA) after 28 days of curing. The maximum compressive strength of 44.1 N/mm2 was achieved using 15% of WPSIA after 60 days of curing. The experimental results presented in this study suggest the potential of WPSIA as a cement replacement. With strength contributing and nontoxic characteristic, the use of WPSIA as a cement replacement may be technically and environmentally feasible. |
|---|---|
| Opis knjige/članka: | https://ir.uitm.edu.my/id/eprint/81688/1/81688.PDF |