Pengembangan Komposit Bermatrik Ebonit Dengan Kandungan Sulfur 30 Phr Yang Diperkuat Serat Kelapa Untuk Komponen Otomotif

This study was aimed to determine the strength of the composite using a variation of fiber weight 0 phr, 30 phr and 50 phr by conducting a tensile test to ASTM D638, Izod test impact with ASTM D256, hardness test with the standard ISO 0778: 2009 and SEM photo by using JEOL JSM-6510LA tool. Composite...

Descrizione completa

Salvato in:

Dettagli Bibliografici
Autori principali:	Anggi Prasetyo, Dika (Autore), , Joko Sedyono, ST, M.Eng, Ph.D (Autore), , Ir. Agus Hariyanto, MT (Autore)
Natura:	Libro
Pubblicazione:	2016-11-05.
Soggetti:	Thesis NonPeerReviewed
Accesso online:	Connect to this object online
Tags:	Aggiungi Tag Nessun Tag, puoi essere il primo ad aggiungerne!!

Documenti analoghi

Pengembangan Komposit Bermatrik Ebonit Dengan Kandungan Sulfur 40 Phr Yang Diperkuat Serat Kelapa Untuk Komponen Otomotif
di: , Isnanto, et al.
Pubblicazione: (2016)

Pengembangan Komposit Bermatrik Ebonit Dengan Kandungan Sulfur 40 Phr Yang Diperkuat Serat Rami 0 Phr, 30 Phr Dan 50 Phr Untuk Komponen Otomotif
di: Puji Nugroho, Prasetyo, et al.
Pubblicazione: (2016)

Pengembangan Komposit Berbahan Ebonit Dengan Kandungan Sulfur 30 PHR Yang Diperkuat Serat Rami Untuk Komponen Otomotif
di: Fawwaz, Fikria, et al.
Pubblicazione: (2017)

Pengembangan Komposit Berbahan Ebonit Dengan Kandungan Sulfur 40 PHR Yang Diperkuat Serat Bambu Untuk Komponen Otomotif
di: Efendi, Rudy, et al.
Pubblicazione: (2017)

Pengembangan Komposit Berbahan Ebonit Dengan Kandungan Sulfur 30 Phr Yang Diperkuat Serat Bambu Untuk Komponen Otomotif
di: Jaya, Rizky Pradhian Putra Rian, et al.
Pubblicazione: (2016)

Studi Pengujian SEM (Scanning Electron Microscopy) Komposit Bermatrik Ebonit Dengan Kandungan Sulfur 40 Phr Yang Diperkuat Serat Rami Dan Bambu Dengan Kandungan Masing-Masing 30 Phr
di: Najakh, Muhammad Abdun, et al.
Pubblicazione: (2017)

Study Pengujian SEM ( Scaning Electron Microscopy ) Pada Ebonit Dengan Kandungan Sulfur 35PHR, Komposit Bermatrik Ebonit Diperkuat Serat Bambu 20PHR Dan 40PHR Serta Spion Honda Scoopy Sebagai Pembanding
di: Narno, Narno, et al.
Pubblicazione: (2016)

Pengembangan Komposit Dari Karet Ebonit Dengan Penguat Serat Serabut Kelapa Untuk Komponen Otomotif Penutup Spion Sepeda Motor
di: Sadewa, Allan Budhi
Pubblicazione: (2016)

Rekayasa Dan Manufaktur Komposit Sandwich Berpenguat Serat Kelapa Bermatrik Epoxy Dengan Core Berpenguat Serat Kelapa Bermatrik Gypsum
di: , Triyono, et al.
Pubblicazione: (2013)

Analisa Foto Makro Dan Sem Pada Komposit Ebonit Dengan Penguat Serat Rami Untuk Pengembangan Komponen Otomotif
di: Nugrahanto, Fajar Agung, et al.
Pubblicazione: (2016)

Pengembangan Komposit Dari Karet Ebonit Dengan Penguat Serat Bambu Untuk Komponen Otomotif Penutup Spion Sepeda Motor
di: Mulyanto, Ade, et al.
Pubblicazione: (2016)

Rekayasa Dan Manufaktur Komposit Skin Berpenguat Serat Kelapa Acak Bermatrik Epoxy
di: Fitriyanto, Wahyu, et al.
Pubblicazione: (2013)

Pengembangan Komposit Dari Karet Ebonit Dengan Penguat Serat Rami Untuk Bahan Komponen Otomotif Penutup Spion Sepeda Motor
di: Altari, Syaifa Maulana
Pubblicazione: (2016)

Rekayasa Dan Manufaktur Komposit CoreBerpenguat Serat Sabut KelapaBermatrik Serbuk Gypsum DenganFraksi Volume Serat 20%, 30%, 40%, 50%
di: Sulistyo, Dwi, et al.
Pubblicazione: (2013)

SIFAT MEKANIK BAHAN GESEK REM KOMPOSIT DIPERKUAT SERAT BAMBU
di: Sutikno -, et al.
Pubblicazione: (2012)

PENGARUH PANJANG SERAT TERHADAP KEAUSAN, KEKUATAN TARIK DAN IMPACT KOMPOSIT SERAT AMPAS TEBU BERMATRIK POLYESTER
di: KURNIAWAN, BUDI
Pubblicazione: (2010)

Karakteristik Komposit Partikel Ijuk Mesh 100 Menggunakan Matrik Karet Dengan Komposisi 0PHR, 10PHR, 20PHR Terhadap Radiasi Sinar Gamma
di: Wahyudi, Sigit, et al.
Pubblicazione: (2016)

PENGARUH KETEBALAN CORE KOMPOSIT SANDWICH BERPENGUAT SERAT RAMI ACAK BERMATRIK EPOXY dengan CORE GYPSUM
di: SUWANTO, TRI
Pubblicazione: (2011)

REKAYASA KOMPOSIT SKIN BERPENGUAT SERAT RAMIE DENGAN PERLAKUAN ALKALI BERMATRIK POLYESTER TERHADAP KEKUATAN MEKANIK
di: SADARTO, AGUS
Pubblicazione: (2011)

Penelitian Pembuatan Rem Komposit Kereta Api Menggunakan Serbuk Pasir Besi Ferro Dan Serat Kulit Kelapa
di: Mahmudi, M. Arif, et al.
Pubblicazione: (2013)

Pengaruh Prosentase Serbuk Arang Batok Kelapa Bermatrik Polyester Pada Komposit Bahan Kampas Rem Sepeda Motor
di: ASMORO, RHONI WIDI
Pubblicazione: (2012)

SINTESIS PAPAN KOMPOSIT BERBAHAN DASAR SERAT SABUT KELAPA DAN SERAT BUAH KETAPANG DENGAN MATRIK PVAc
di: Susilawati Susilawati, et al.
Pubblicazione: (2020)

Analisis Komposit Dengan Penguat Serat Rami 40% Dan Serbuk Kayu Sengon 60% Pada Fraksi Volume 40%,50%,60% Bermatrik Resin Polyester Untuk Panel Akuistik
di: Pradika, Leody Ilham, et al.
Pubblicazione: (2016)

Rekayasa Komposit Berpenguat Serat Rami Acak Bermatrik Epoxy Terhadap Sifat Fisik dan Mekanik dengan Fraksi Volume Serat 20%, 30%, 40%, 50%
di: Prasetyo, David Dwi
Pubblicazione: (2011)

Karakteristik Komposit Serat Kulit Waru Yang Disusun Laminasi Bermatrik Polyester Dengan Orientasi Serat [ 60 / 65 /70 ] Terhadap Sifat Fisis Dan Mekanis
di: Anggoro, Bayu Pebri, et al.
Pubblicazione: (2016)

Rekayasa Komposit Sandwich Berpenguat Serat Rami dan Sekam Padi Bermatrik Polyester dan Urea Formaldehide Terhadap kekuatan Mekanik
di: SULAKSONO, BIMO ADITYA
Pubblicazione: (2011)

Analisa Pengujian Tarik Pipa Komposit Serat Batang Pisang Bermatrik Polyester Bqtn 157 Dengan Sudut Serat 65/-65 Pada Variasi Temperatur Ruang Uji
di: Wibisono, Reza Riyantoko, et al.
Pubblicazione: (2015)

STUDI PEMBUATAN KOMPOSIT ALAMI DENGAN BAHAN EBONIT DAN KENAF
di: ARDI, FAESAL
Pubblicazione: (2010)

STUDI EKSPERIMENTAL KOMPOSIT ALAMI DENGAN BAHAN EBONIT DAN BAMBU
di: PRASETYA, EKO
Pubblicazione: (2010)

Pengaruh Komposit Partikel Ijuk Mesh 100 Menggunakan Karet Terhadap Radiasi Sinar Gamma Dengan Komposisi Serbuk Ijuk 0 Phr, 15 Phr, 25phr
di: Sutrisno, Sutrisno, et al.
Pubblicazione: (2016)

PENGARUH FRAKSI VOLUME KOMPOSIT BERPENGUAT SERAT RAMI ACAK BERMATRIK POLYESTER BQTN 157 DAN SERAT E-GLASS ACAK TANPA PERLAKUAN ALKALI TERHADAP KEKUATAN MEKANIK
di: IRWANTOKO, OKI
Pubblicazione: (2011)

Sifat Fisis Dan Mekanis Akibat Perubahan Temperatur Pada Komposit Serat Batang Pisang Yang Dicuci Menggunakan Naoh Bermatrik Epoxy
di: Kusdiyanto, Kusdiyanto, et al.
Pubblicazione: (2014)

Analisa Lembaran Komposit berpenguat Serbuk Ijuk mesh 60 Menggunakan Matrik Karet Terhadap Radiasi Sinar Gamma Dengan variasi Komposisi Serbuk Ijuk 0 Phr, 15 Phr, 25 Phr
di: Prasetyo, Hari, et al.
Pubblicazione: (2016)

Karakteristik Komposit Partikel Ijuk Mesh 40 Menggunakan Matrik Karet Dengan Variasi Komposisi Serbuk Ijuk 0 Phr,15 Phr,25 Phr Terhadap Daya Serap Radiasi Sinar Gamma
di: Priyono, Kukuh Suko, et al.
Pubblicazione: (2016)

PENELETIAN PEMBUATAN REM KOMPOSIT KERETA API MENGGUNAKAN SERBUK PASIR BESI NON FERRO DAN SERAT KULIT KELAPA
di: PURWANTO, PURWANTO
Pubblicazione: (2011)

STUDI SHRINKAGE DAN KEKUATAN BENDING PADA PEMBUATAN HANDLE MOBIL DARI BAHAN CAMPURAN ANTARA EBONIT DENGAN SERATBAMBU DAN EBONIT DENGAN SERAT KENAF
di: GHANI, YUDHA ARIEF
Pubblicazione: (2010)

Analisa Lembaran Komposit Berpenguat Serbuk Ijuk Mesh 40 Menggunakan Matrik Karet Alam Dengan Variasi Komposisi Serbuk Ijuk 0 PHR, 10 PHR, 20 PHR Terhadap Daya Serap Radiasi Sinar Gamma
di: Wibowo, Arif Adi, et al.
Pubblicazione: (2016)

ANALISIS KEKUATAN TARIK KOMPOSIT PET (Polyethylene Terephthalate) DENGAN FRAKSI VOLUME MENGGUNAKAN RESIN EPOKSI DAN SERAT KELAPA SAWIT
di: Tiara Dewi Nabilah Farihah,
Pubblicazione: (2023)

Analisa Lembaran Komposit Berpenguat Serbuk Ijuk Mesh 60 Menggunakan Matrik Karet Alam Dengan Variasi Komposisi Serbuk Ijuk (0, 10, 20) Phr Terhadap Radiasi Sinar Gamma
di: Faid, Anim Nur, et al.
Pubblicazione: (2016)

Pengaruh Kandungan Komponen Minor dari Minyak Kelapa Sawit (Elaeis guineensis Jacq.) Terhadap Aktivitas Antioksidan pada Proses Pemurnian Karotenoid
di: Ahmad Gazali Sofwan Sinaga, et al.
Pubblicazione: (2015)